抄録

A visible-light-responsive photocatalyst has been prepared simply by sintering a TiO₂-coated Cu plate. The new photocatalyst was able to reduce the concentration of formaldehyde by 8-12% at ca. 296K with an air flow rate of ca. 0.5 L/min (ca. 1ppm formaldehyde included), a photocatalyst cross section of 50 × 100mm², ca. 50% humidity, and light intensity of 30W/m² (white LED light). The reduction rate was approximately two times higher than that for N-doped TiO₂ (TiO_2-xN _x) under almost the same test conditions.

本文言語	英語
論文番号	098001
ジャーナル	Japanese Journal of Applied Physics
巻	53
号	9
DOI	https://doi.org/10.7567/JJAP.53.098001
出版ステータス	出版済み - 2014

文献へのアクセス

10.7567/JJAP.53.098001

他のファイルとリンク

Scopusの出版物のリンク

引用スタイル

@article{618cb87ab116431696f44979fa5fd690,

title = "Visible-light-responsive photocatalyst prepared by sintering a TiO 2/Cu plate",

abstract = "A visible-light-responsive photocatalyst has been prepared simply by sintering a TiO2-coated Cu plate. The new photocatalyst was able to reduce the concentration of formaldehyde by 8-12\% at ca. 296K with an air flow rate of ca. 0.5 L/min (ca. 1ppm formaldehyde included), a photocatalyst cross section of 50 × 100mm2, ca. 50\% humidity, and light intensity of 30W/m2 (white LED light). The reduction rate was approximately two times higher than that for N-doped TiO2 (TiO2-xN x) under almost the same test conditions.",

author = "Sumio Kogoshi and Syota Araki and Syota Yazawa and Takuma Nakano and Tomohiko Takeuchi and Noboru Katayama and Yusuke Kudo and Tetsuya Nakanishi",

year = "2014",

doi = "10.7567/JJAP.53.098001",

language = "English",

volume = "53",

journal = "Japanese Journal of Applied Physics",

issn = "0021-4922",

publisher = "Institute of Physics",

number = "9",

}

TY - JOUR

T1 - Visible-light-responsive photocatalyst prepared by sintering a TiO 2/Cu plate

AU - Kogoshi, Sumio

AU - Araki, Syota

AU - Yazawa, Syota

AU - Nakano, Takuma

AU - Takeuchi, Tomohiko

AU - Katayama, Noboru

AU - Kudo, Yusuke

AU - Nakanishi, Tetsuya

PY - 2014

Y1 - 2014

N2 - A visible-light-responsive photocatalyst has been prepared simply by sintering a TiO2-coated Cu plate. The new photocatalyst was able to reduce the concentration of formaldehyde by 8-12% at ca. 296K with an air flow rate of ca. 0.5 L/min (ca. 1ppm formaldehyde included), a photocatalyst cross section of 50 × 100mm2, ca. 50% humidity, and light intensity of 30W/m2 (white LED light). The reduction rate was approximately two times higher than that for N-doped TiO2 (TiO2-xN x) under almost the same test conditions.

AB - A visible-light-responsive photocatalyst has been prepared simply by sintering a TiO2-coated Cu plate. The new photocatalyst was able to reduce the concentration of formaldehyde by 8-12% at ca. 296K with an air flow rate of ca. 0.5 L/min (ca. 1ppm formaldehyde included), a photocatalyst cross section of 50 × 100mm2, ca. 50% humidity, and light intensity of 30W/m2 (white LED light). The reduction rate was approximately two times higher than that for N-doped TiO2 (TiO2-xN x) under almost the same test conditions.

UR - https://www.scopus.com/pages/publications/84906871514

U2 - 10.7567/JJAP.53.098001

DO - 10.7567/JJAP.53.098001

M3 - Article

AN - SCOPUS:84906871514

SN - 0021-4922

VL - 53

JO - Japanese Journal of Applied Physics

JF - Japanese Journal of Applied Physics

IS - 9

M1 - 098001

ER -

Visible-light-responsive photocatalyst prepared by sintering a TiO 2/Cu plate

抄録

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル

Visible-light-responsive photocatalyst prepared by sintering a TiO ₂/Cu plate