Influence of pre-etched area and functional monomers on the enamel bond strength of orthodontic adhesive pastes

Yuriko Tezuka, Yasuhiro Namura, Akihisa Utsu, Kiyotaka Wake, Yasuki Uchida, Mizuki Inaba, Toshiki Takamizawa, Mitsuru Motoyoshi

Research output: Contribution to journalArticlepeer-review

Abstract

This study was performed to investigate the influence of pre-etching area and functional monomers in orthodontic adhesive pastes on enamel bond strength. Bovine enamel was partially pre-etched with phosphoric acid for 30 s over areas with a diameter of 1.0, 2.0 or 3.0 mm, and metal brackets were then bonded with or without functional monomers in the orthodontic adhesive paste. For the baseline groups, the whole adherent area was pre-etched. The shear bond strength (SBS) and adhesive remnant index (ARI) were determined. The adhesive paste/enamel interfaces were observed by scanning electron microscopy (SEM). Although the adhesive paste with functional monomers showed higher SBS than the functional monomer-free adhesive paste in all groups, there were no significant differences in SBS between them regardless of the pre-etched area. The SBS increased with increasing pre-etched area in both orthodontic adhesive pastes. In SEM images of adhesive paste/enamel interfaces, although adhesive with functional monomers showed excellent adaptation, the functional monomer-free adhesive paste showed gap formation at the interface. These findings suggested that the pre-etching area greatly influenced bond strength, regardless of the presence or absence of the functional monomer in the orthodontic adhesive paste.

Original languageEnglish
Article number8251
JournalApplied Sciences (Switzerland)
Volume11
Issue number17
DOIs
Publication statusPublished - Sept 2021

Keywords

  • Functional monomer
  • Orthodontic adhesive paste
  • Pre-etched area

Fingerprint

Dive into the research topics of 'Influence of pre-etched area and functional monomers on the enamel bond strength of orthodontic adhesive pastes'. Together they form a unique fingerprint.

Cite this